AWS: E 6012
ISO: E 433 R 12
DIN EN 499: E 350 RC
DIN 1913: E 43 22 R(C)3
Current: = (-) / ~ |
|
|
Medium coated electrode for normal steel structures. It is particularly suited for welding poorly accessible parts and badly prepared seams.
The electrode welds well for all positions and is especially developed for welding vertical down. Easy slag removal, viscous weld metal gives good gap bridging.
Suitable for following base materials:
St 34-52, St 35-45, GS 38-45
shipbuilding steel A-D, H I, H II
|
|
|
T: 470 – 520 N/mm²
Y: 410 – 450 N/mm²
E(1=5d): 20 – 25 %
I: 60 – 90 Joule |
|
 |
|
|
|
AWS: E 6012
ISO: E 433 R 12
DIN EN 499: E 350 RC
DIN 1913: E 43 21 R(C)3
Current: = (-) / ~ |
|
|
The electrode has a wide range of application in shipbuilding, automobile industry, mechanical engineering.
The electrode is particularly suitable for field welding as the resulting weld deposit is crack resistant. The specially formulated coating gives excellent bead shape in all applications. Easy striking and arcing. Smooth welding characteristics. Easy slag removal.
Suitable for following base materials:
St 34-52, St 35-45, GS 38-45
shipbuilding steel A-D, H I, H II
|
|
|
T: 470 – 520 N/mm²
Y: 410 – 450 N/mm²
E(1=5d): 20 – 25 %
I: 60 – 90 Joule |
|
|
|
|
|
AWS: E 6012 / 6013
ISO: E 433 R 12
DIN EN 499: E 350 RC
DIN 1913: E 43 21 R(C)3
BS: E 217
Current: = (+) / ~ |
|
|
The electrode is thick coated for joining steel structures of all kinds in mechanical engineering and steel structures.
The electrode is particularly suitable for field welding as the resulting weld deposit is crack resistant. The specially formulated coating gives excellent bead shape in all applications. Easy striking and arcing. Smooth welding characteristics. Easy slag removal.
Suitable for following base materials:
St 34-52, St 35-45, GS 38-45
shipbuilding steel A-D, H I, H II
|
|
|
T: 470 – 520 N/mm²
Y: 410 – 450 N/mm²
E(1=5d): 20 – 25 %
I: 60 – 90 Joule |
|
|
|
|
|
AWS: E 6013
ISO: E 513 RR 23
DIN EN 499: E 420 RR
DIN 1913: E 51 22 RR 6
Current: = (-) / ~ |
|
|
The electrode is thick coated for joining steel structures of all kinds in mechanical engineering, body and wagon building, in the fabrication of vessels and containers in shipbuilding.
It is particularly suited for welding thin sheets. The weld deposit can be galvanized and enamelled.
The electrode is easily weldable and has excellent welding properties in all positions except vertical down. Easy ignition, uniform flow , no spatter. Easy slag removal, fine rippled seam surface.
Suitable for following base materials:
St 34-52, St 35-45, GS 38-52
Shipbuilding steel A-E, H I, H II.
|
|
|
T: 480 – 520 N/mm²
Y: 410 – 450 N/mm²
E(1=5d): 23 – 26 %
I: 60 – 90 Joule |
|
|
|
|
|
AWS: E 7018
ISO: E 514 B 120 26
DIN EN 499:E 422 B 3
DIN 1913: E 51 53 B 10
Current: = (+) / ~ |
|
|
Lime-basic coated electrode for tough and crack resistant weld joints. The weld deposit is non-ageing. Especially usable for steels with max. 0,45% C and also for base materials with higher contents of P and S. Recovery 120 %. Weldable with DC (+) and with AC if open circuit voltage is minimum 65 V.
Suitable for following base materials:
St 34-52, St 35-55, St 50, St 60, GS 38-52
Shipbuilding steel A-E, H I, H II, H III, 17 Mn 4
|
|
|
T: 550 – 630 N/mm²
Y: 450 – 500 N/mm²
E(1=5d): 25 – 30 %
I: 120 – 170 Joule |
|
|
|
|
|
AWS: E 6012 / 7013
DIN 1913: E 51 22 RR 6
Current: = (-) / ~ |
|
|
Coated electrode in general used for welding of joints in the sheet processing industry. Especially suitable for welding at acute angles and in tacking work
Suitable for following base materials:
St 34-52, St 35.4, St 45.8
shipbuilding steel A-D, H I, H II
|
|
|
T: 480 – 520 N/mm²
Y: 410 – 450 N/mm²
E(1=5d): 23 – 26 %
I: 100 – 130 Joule |
|
|
|
|
|
AWS: E 6013
DIN 1913: E 43 32 AR 7
Current: = (-) / ~ |
|
|
It is an electrode recommended for applications where moderate penetration is desirable. The electrode has very stable arc and good bead appearance when use with either AC or DC power sources.
Suitable for following base materials:
St 34-52, St 35-45, St 45.8
shipbuilding steel A, H I, H II
|
|
|
T: 470 – 520 N/mm²
Y: 370 – 480 N/mm²
E(1=5d): 23 – 26 %
I: 70 – 100 Joule |
|
|
|
|
|
AWS: E 7016
ISO: E 433 B 26
DIN EN 499:E 38 2 B
DIN 1913: E 51 43 B(R) 10
Current: = (+) / ~ |
|
|
Lime-basic double coated electrode with excellent weldabilty, especially on AC. No reinforcement, no undercut, equal sided weld deposit.
Well suited for welding difficult positions, easy slag removal.
Suitable for following base materials:
St 34-52, St 35-55, St 50, St 60, GS 38-52
shipbuilding steel A-D, H I, H II, H III, H IV, 17 Mn 4, 19 Mn 5
|
|
|
T: 530 – 580 N/mm²
Y: 430 – 490 N/mm²
E(1=5d): 28 – 32 %
I: 110 – 150 Joule |
|
|
|
|
|
AWS: E 7018
ISO: E 514 B 120 26
DIN EN 499:E 423 B 3
DIN 1913: E 51 54 B 10
Current: = (+) / ~ |
|
|
Lime-basic electrode with higher strength. Especially crack resistant, non ageing and tough down – 60ºC.
Recovery 120%. Fine rippled seam surface, no undercut & weldable with DC (+) and AC. Good weldability in difficult positions.
Suitable for following base materials
St 34-52, St 35-55, St 50, St 60, St 70, GS 38-52
shipbuilding steel A-E, H I, H II, H III, H IV, 17 Mn 4, 19 Mn 5
|
|
|
T: 570 – 650 N/mm²
Y: 470 – 510 N/mm²
E(1=5d): 25 – 30 %
I: 120 – 170 Joule |
|
|
|
|
|
AWS: E 6024
ISO: E 513 RR 160 22
DIN EN 499:E 420 RR 5
DIN 1913:E 51 32 RR 11 160
Current: = (-) / ~ |
|
|
Rutile-coated high efficiency electrode with a recovery of 160%.
Long single passes are possible. Easy strike and re-strike, spatter loss is low, good slag removal, no undercuts. Typical applications are railroad cars, ship building and earth moving equipment.
Suitable for following base materials:
St 34-52, St GS 38-52
Shipbuilding steel A-D, H I, H II, H III, 17 Mn 4
fine grain constructional steel with 500 – 600 N/mm2
|
|
|
T: 480 – 520 N/mm²
Y: 420 – 460 N/mm²
E(1=5d): 23 – 26 %
I: 70 – 90 Joule |
|
|