Hardfacing products available on request

Product
Standard
Weld Metal Analysis
Applications
Mechanical Properties
E 250 Kb
DIN 8555:
E 1 – UM – 250 – P

EN 14700: E Fe 1

Current: = (+) / ~
C: 0,1

Mn: 1,5

Cr: 1,0

Lime basic electrode for overlays on rails, rollers etc., machinable.

Hard surfacing of parts which need to be machined and which, in service, are subject to high compression stress and high impact. Can be applied in several layers. Used as buffer electrode when surfacing is carried out with electrodes showing higher abrasion resistance. Examples: buffer layer-rebuilding of worn parts such as rollers, wheels and guides encountered in the earth movig field.
H: 225 – 275 HB
Table separator
E 300 Kb
DIN 8555:
E 1 – UM – 300 – P

EN 14700: E Fe 1

Current: = (+) / ~
C: 0,1

Mn: 1,0

Cr: 3

Lime basic coated electrode, especially for overlays on low-alloyed steels up 900 N/mm2 tensile strength.

Hard surfacing of parts which need to be machined and which, in service, are subject to high compression stress and high impact. Can be applied in several layers. Used as buffer electrode when surfacing is carried out with electrodes showing higher abrasion resistance. Examples: buffer layer-rebuilding of worn parts such as rollers, wheels and guides encountered in the Earth moving field.
H: 275 – 325 HB
Table separator
E 58 Kb
DIN 8555:
E 6 – UM – 60 – F

EN 14700: E Fe 8
Lime basic electrode for very high impact loads. Can also be welded in verical down position.
H: 550 – 600 HB
Table separator
E 580
DIN 8555:E 2 – UM – 60

EN 14700: E Fe 4

Current: = (+) / ~
C: 1,5

Cr:3

Others:+

Rutile – basic coated electrode for overlays on machine parts with high impact load. subject to abrasion.

The weld metal of E 580 is tough, hard and abrsion proof, hardfacing on strucctural steel, cast steel and austenitic magneese steel. The weld metal is non porous and free from cracks. It can be used for multiple layer hardfacing. Typical examples: Dredger teeth, crusher jaws, crushing heads, impact strips, crushing rings and guides.
H: 550 – 620 HB
Table separator
Metadur 50
DIN 8555:
E 3 – UM – 50 – T

Current: = (+) / ~

Rutile basic coated electrode for tough overlays, resistant to wear. The weld deposit is high temperature resistant and self tempering.
H: 50 – 53 HRc
Table separator
SS 61
DIN 8555:
E 4 – UM – 60/65 – ST
Thick coated elctrode for armouring of cutting edges on tools made of unalloyed steel.
H:60 – 63HRc untreat

63 – 66HRc annealed

Table separator
SS 62
DIN 8555:
E 4 – UM – 60/65 – ST
Thick coated elctrode for overlays on tools. Also suited for wear resistant overlays.
H:60 – 63HRc untreat

63 – 66HRc annealed
Table separator
Cronimangan
DIN 8555:
E 7 – UM – 200 – K
Lime-basic coated electrode for tough overlays, resistant to wear.
H: max. 470 HB
Table separator
Manganchrom
DIN 8555:
E 8 – UM – 250 – KPN
Lime – basic coated electrode for buffer layers, rails, rail crossings, crusher jaws.
H: 450 – 550HB
Table separator
4324 HL
DIN 8555:
E 9 – UM – 200 – K

EN 14700: E Fe 11

Recovery: 160%

Current: = (+) / ~

C : 0,25

Cr: 19

Ni: 9

Mn: 2,5
Rutile basic coated electrode with 160% recovery. For covering intermediate layers.

Temperature resistant up to 900 ºC. Rust and corrison resistant.
H: 200 – 250 HB

after cold hardening: 450 HB
Table separator
NiCoMo
DIN 8555:
E 4 – UM – 350 – S
Rutile basic electrode for coating of forging dies. heat resistant, Fe based alloys with high contenet of Ni, Co and Mo.
H: 320 – 350HB
Table separator
Metadur 6 Ni
DIN 8555:
E 22 – UM – 40 – CTZ

EN 14700: E Ni 4

Current: = (+) / ~
C: 0,02

Si: 3

Cr: 9

Ni: Rest
Lime-coated nickel based electrode for overlays similar to satellite alloys, see “special electrode with high nickel content”.
H: ca. 40 HRc

heat resistant like stellites

Table separator
Metadur 59
DIN 8555:
E 10 – UM- 60 -Z
Very thick coated electrode for high wear resistant overlays. Slag does not cover the weld deposit.

Applications are constructional and machine parts, that are subject to heavy abrasion and moderate impacts .e.g. mixer parts and sand blasting equipment, descaling units etc.
H: 58 – 62 HRc
Table separator
Metadur 60 V
DIN 8555:
E 10 – UM – 60 – Z
A hardfacing electrode, developed on a chrome-carbide basis for abrasive wear and medium impact stressing, e.g by ores, coal gravels sand, for overlaying on excavator teeth, wear strips, screw conyeyors etc. Also useable for guideways, valve ends and machine parts to operating temperature up to 200 ºC.

The clear weld pool permits better bead build up, so that post weld machining is not necessary, Easy slag removal.
H: 57 – 60 HRc
Table separator
Metadur 61
DIN 8555:
E 10 – UM – 65 – Z

EN 14700: E Fe 16

Recovery: 170%
Electrode with 170% recovery, for highly wear resistant overlays, no slag.
H: 62 – 66 HRc
Table separator
Metadur 61 B
DIN 8555:
E 10 – UM – 65 – Z

EN 14700: E Fe 16

Recovery: 170%
Electrode with 170% recovery,for highly wear resistant overlays, no slag and high basic hardness in the first layer 62Hrc already.
H: 63 – 67 HRc
Table separator
Metadur 63 Super
DIN 8555:
E 10 – UM – 65 – Z

EN 14700: E Fe 16

Recovery: 200%
Electrodes with 200% recovery, high wear resistant still > 40 HRc at 600 ºC.
H: 62 – 65 HRc
Table separator
Metadur 64
DIN 8555:
E 10 – UM – 65 – Z

EN 14700: E Fe 16
Cr-W-V-Nb Carbide
Very thick coated electrode for high wear resistant overlays which are subject to abrasion.
H: 62 – 65 HRc
Table separator
Metadur 64 i
DIN 8555:
E 10 – UM – 65 – GR Z

EN 14700: E Fe 16
Cr-Nb-W-V-Carbide
Hardfacing electrode with extraordinarily good resistance to wear. Also suited for higher temperatures.
H: 61 -64 HRc
Table separator
Metadur 64 S
DIN 8555:
E 10 – UM – 65 – GRZ

EN 14700: E Fe 16
Cr -W-V-Nb Carbides
It is an extra hard surfacing electrode for wear resistant overlays which are subject to extremely severe abrasion by sand gravel, ore, coal, cement or slag.

Very thick coated electrode for high wear resistant overlays which are subject to abrasion. Therefore it is suitable for hardfacing in crushing plants, scraping leaks for the zinc industry, blast furnace hinging equipment and palm nut press screws. In case of more than 3layers the bottom layers should be welded with E 350Kb.

H: 62 – 65 HRc
Table separator
Metadur 65
DIN 8555:
E 10 – UM – 65 – GRZ

EN 14700: E Fe 16
Cr-Nb-W-V-Carbide
Hardfacing electrode with extraordinarily good resistance to wear.
H: 63 – 66 HRc
Table separator
Metadur 65 S
DIN 8555:
E 10 – UM – 65 – GRZ

EN 14700: E Fe 16
Cr-W-V-Nb Carbides
Resists very severe abrasion at temperatures up to 1400F (760ºC). Exhibit the highest abrasion resistance of the Wear shield stick electrodes. Premium complex carbide deposit.
H: 65 – 66 HRc
Table separator
Metasecure
DIN 8555:
E 10 – UM – 60 -Z
-
Special electrode for overlays on rolls in the Sugar Cane industry.
H: 55 – 60 HRc
Table separator
E 40 Cr 12
DIN 8555: E 6-40

Recovery: 130%

Current: = (+) / ~
C: 1

Cr: 12
Lime basic electrode for hardfacing which are subject to hard wear and impact loads. It is possible to weld thicker layers with this tough and hard material.
H: 37 – 43 HB
Table separator

Latest News

Pages

Categories

  • No categories

Little About Us

Hello Read More »

Cheap Jerseys Cheap Jerseys/ Cheap Jerseys Cheap Jerseys Cheap Jerseys Cheap Jerseys Cheap Jerseys Cheap Jerseys Cheap Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys