High recovery electrodes for corrosion resistant CrNi and CrNiMo steels

Product
Standard
Weld Metal Analysis
Applications
Mechanical Properties
4302 HL
AWS: E 308 – 26

DIN 8556:
E 19 9 MPR 26 150

EN 1600:E 19 9 R 52

EN ISO 3581:E 19.9 R 25

Recovery: 150%

Current: = (+) / ~

C: 0,06

Cr: 17 – 20

Ni: 8,0 – 10,5
For CrNi-steels type 18-8. The weld deposit is capable of taking a high polish. Working temperatures up to 300 ºC.

Suitable for following base materials:
1.4300, 1.4308, 1.4310, 1.4312, 1.4550, 1.4001, 1.4016, 1.4057
T: 540 – 650 N/mm²

Y: 310 – 350 N/mm²

E(1=5d): 35 %

I: 70 – 90 Joule
Table separator
4316 HL
AWS: E 308 L – 26

DIN 8556:
E 19 9 L MPR 26 150

EN 1600:E 19 9 L R 52

EN ISO 3581:E 19.9 L R 25

Recovery: 150%

Current: = (+) / ~

C: 0,02

Cr: 19

Ni: 8,0 – 10,5
For CrNi-steels type 18-8 with low C-content. The weld deposit is capable of taking a high polish. Working temperatures up to 400 ºC.

Suitable for following base materials:
1.4300, 1.4301, 1.4306, 1.4541, 1.4543, 1.4550
T: 530 N/mm²

Y: 310 N/mm²

E(1=5d): 37 %

I: 80 Joule
Table separator
4403 HL
AWS: E 316 – 26

DIN 8556:E 19 12 3 MPR 26 150

EN 1600:E 19 12 3 R 52

EN ISO 3581:E 19.12.3 R 25

Recovery: 160%

Current: = (+) / ~

C: 0.05

Cr: 19

Ni: 12

Mo: 2,7

For CrNiMo-steels type 18-8-2. The weld deposit is capable of taking a high polish. Working temperatures up to 300 ºC.

Suitable for following base materials:
1.4401, 1.4436, 1.4413
T: 540 N/mm²

Y: 310 N/mm²

E(1=5d): 35 %

I: 75 Joule

Table separator
4430 HL
AWS: 316 L – 26

DIN 8556:
E 19 12 3 L MPR 26 150

EN 1600:E 19 12 3 L R 52

EN ISO 3581:
E 19.12.3 L R 25

Recovery: 160%

Current: = (+) / ~

C: 0,03

Cr: 19

Ni: 12

Mo: 2,7
For CrNiMo-steels type 18-8-2 with low C-content. The weld deposit is capable of taking a high polish. Working temperatures up to 400 ºC.

Suitable for following base materials:
1.4401, 1.4404, 1.4435, 1.4436, 1.4571, 1.4573, 1.4580, 1.4583
T: 540 N/mm²

Y: 310 N/mm²

E(1=5d): 35 %

I: 75 Joule
Table separator
4502 HL
AWS: E 430 – 26

DIN 8556: E 17 MPR 26 150

EN 1600: E 17 R 52

EN ISO 3581:E 17 R 25

Recovery: 160%

For joint weldings and overlays on chromium steels of same kind. Especially suitable for rail overlay welding.
Table separator
4551 HL
AWS: E 347 – 26

DIN 8556: E 19 9 Nb MPR 26 150

EN 1600: E 19 9 Nb R 52

EN ISO 3581:E 19.9 Nb R 25

Recovery: 150%

Current: = (+) / ~

C: 0.05

Cr: 19

Ni: 9,5

Nb:+

For stablized CrNi-steels type 18-8. Working temperatures up to 400 ºC.

Suitable for following base materials:
1.4301, 1.4310, 1.4541, 1.4543, 1.4550, 1.4878
T: 570 N/mm²

Y: 340 N/mm²

E(1=5d): 32 %

I: 75 Joule

Table separator
4576 HL
AWS: E 318 – 26

DIN 8556: E 19 12 3 Nb MPR 26 150

EN 1600: E 19 12 3 Nb R 52

EN ISO 3581:E 19.12.3 Nb R 25

Recovery: 160%

Current: = (+) / ~

C: 0.05

Cr: 19

Ni: 11,5

Nb: +

For stablized CrNiMo-steels type 18-8-2. Working temperatures up to 400 ºC.

Suitable for following base materials:
1,4401, 1,4404, 1,4435, 1,4436, 1, 4571, 1,4573, 1,4580

T: 570 N/mm²

Y: 360 N/mm²

E(1=5d): 32 %

I: 75 Joule

Table separator
4829 HL
AWS: E 309 L – 26

DIN 8556:E 22 12 MPR 26 160

EN 1600: E 22 12 R 52

EN ISO 3581:E 22.12 R 25

Recovery: 160%

Current: = (+) / ~

C: 0.05

Cr: 22

Ni: 12

For joint welds on heat resistant steels of same kind.Scale resistant up to 1050 ºC.

Suitable for following base materials:
1.4742, 1.4826, 1.4828.
T: 540 N/mm²

Y: 310 N/mm²

E(1=5d): 35 %

I: 75 Joule
Table separator
4829 Mo HL
AWS: E 309 Mo – 26

DIN 8556: E 22 12 3 MPR 26 170

EN 1600: E 23 12 2 R 72

EN ISO 3581:E 23.12.2 R 27

Recovery: 160%

For joint welds on heat-resistant steels of same kind as well as high alloyed and unalloyed steels. Scale resistant up to 1100 ºC.

Suitable for following base materials:
1.4742, 1.4826, 1.4828.
T: 540 N/mm²

Y: 340 N/mm²

E(1=5d): 35 %

I: 75 Joule

Table separator
4842 HL
AWS: E 310 – 26

DIN 8556:E 25 20 MPR 26 160

EN 1600: E 25 20 R 52

EN ISO 3581:E 25.20 R 25

Recovery: 170%

Current: = (+) / ~
C: 0,10

Cr: 25

Ni: 20
For joint welds on heat resistant CrNi-steels of same kind. Scale resistant up to 1200 ºC.

Suitable for following base materials:
1.4762, 1.4841, 1.4845, 1.4846, 1.4848, 1.4849
T: 590 N/mm²

Y: 340 N/mm²

E(1=5d): 30 %

I: 70 Joule
Table separator
4316 HLS
AWS: E 308L – 26

DIN 8556: E 19 9 L R 26 150

EN 1600: E 19 9 L R 52

EN ISO 3581:E 19.9 L R 25

Current: = (+) / ~

C: 0.02

Cr: 19

Ni: 8 – 10,5

For CrNi-steels type 18-8. The weld deposit is capable of taking a high polish. Working tempetatures up to 350 ºC.

Suitable for following base materials:
1.4300, 1.4301, 1.4306, 1.4541, 1.4543, 1.4550

T: 530 N/mm²

Y: 310 N/mm²

E(1=5d): 37 %

I: 80 Joule

Table separator
4302 HLS
AWS: E 308 – 16

DIN 8556:E 19 9 R 26 150

Recovery: 150%

 C: 0.06

Cr: 17 – 20

Ni: 8 – 10,5

Electrodes for welding of joints and overlays on 18/8Cr Ni-steels. The welding material is capable of taking a high polish. Suitable for working temperatures up to 300 ºC(570 ºF).

Particularly soft and regularly melting. Agreeable for the welder. Stable arc, even at low currents on thin plates.

Suitable for following base materials:
1.4300, 1.4308, 1.4310, 1.4312, 1.4550, 1.4001, 1.4016, 1.4057

T: 540 – 650 N/mm²

Y: 310 – 350 N/mm²

E(1=5d): 35 %

I: 70 – 90 Joule
Table separator
4430 HLS
AWS: E 316L – 26

DIN 8556:
E 19 12 3 L R 26 160

EN 1600:E 19 12 3 L R 52

EN ISO 3581:E 19.12.3 L R 25

Recovery: 160%

 C: 0.03

Cr: 19

Ni: 12

Mo: 2,7

For CrNiMo-steels type 18-8-2 with low C-content. The weld deposit is capable of taking a high polish. Working temperatures up to 350 ºC.

Suitable for following base materials:
1.4401, 1.4404, 1.4435, 1.4436, 1.4571, 1.4573, 1.4580, 1.4583

T: 540 N/mm²

Y: 310 N/mm²

E(1=5d): 35 %

I: 75 Joule
Table separator
4551 HLS
AWS: E 347 – 26

DIN 8556:
E 19 9 Nb MPR 26 160

EN 1600:E 19 9 Nb R 52

EN ISO 3581:E 19.9 Nb R 25

Recovery: 150%

Current: = (+) / ~

 C: 0,05

Cr: 19

Ni: 9,5

Nb: +

For stabilized CrNi-steels type 18-8. Working up to 400 ºC.

Suitable for following base materials:
1.4301, 1.4310, 1.4541, 1.4543, 1.4550, 1.4878

 T: 570 N/mm²

Y: 340 N/mm²

E(1=5d): 32 %

I: 75 Joule

Table separator
4576 HLS
AWS: E 318 – 26

DIN 8556:
E 19 12 3 MPR 26 160

EN 1600:E 19 12 3 Nb R 52

EN ISO 3581:
E 19.12.3 Nb R 25

Recovery: 160%

Current: = (+) / ~
C: 0,05

Cr: 19

Ni: 11,5

Mo: 2,7

Nb: +
For stabilized CrNiMo-steels type 18-8-2. Working temperatures up to 400 ºC.

Suitable for following base materials:
1,4401, 1,4404, 1,4435, 1,4436, 1, 4571, 1,4573, 1,4580

T: 570 N/mm²

Y: 360 N/mm²

E(1=5d): 32 %

I: 70 Joule
Table separator
4842 HLS
AWS: E 310 – 26

DIN 8556:
E 25 20 MPR 26 170

EN 1600:
E 25 20 R 72

EN ISO 3581:E 25.20 R 27

Recovery: 170%

Current: = (+) / ~
 C: 0,10

Cr: 25

Ni: 20

For joint welds on heat resistant Cr-Ni-steels of same kind. Scale resistant up to 1200 ºC.

Welding of the 25 Cr-20 Ni refractory steels whose alloy contents are between 20 and 27% chromium, 18 and 22% nickel, such as the AlSi 310, 310L and 405 steels.

Especially recommended for welding sheets and medium-thick plates.

Suitable for following base materials:
1.4762, 1.4841, 1.485, 1.4846, 1.4848, 1.4849

T: 590 N/mm²

Y: 340 N/mm²

E(1=5d): 30 %

I: 70 Joule
Table separator

Latest News

Pages

Categories

  • No categories

Little About Us

Hello Read More »

Cheap Jerseys Cheap Jerseys/ Cheap Jerseys Cheap Jerseys Cheap Jerseys Cheap Jerseys Cheap Jerseys Cheap Jerseys Cheap Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys