Electrodes for low-alloyed steels

Product
Standard
Weld Metal Analysis
Applications
Mechanical Properties
Mo
AWS: E Ni Cu B

DIN 8573: E Ni Cu G 2

Current: = (+) / ~

-
A successful electrode for “cold” welding grey, malleable and cast iron. Special thin coating for minimum heat insures fully machinable deposit, completely free from porosity.
T: 240 – 290 N/mm²————–

H: 190 HB

Table separator
Mo Ti
AWS: E 7013 G

ISO 3580: E Mo R

DIN 8575: E Mo R 22

-

Rutile-basic coated electrode for high tensile and high temperature steel. The weld deposit is tough and non-ageing.

Suitable for materials:
St45,8, St50, St55,4, 17Mn4, 19Mn5, 15Mo3, HIII, HIV, WStE 36

T: 520 – 620 N/mm²

Y: 440 – 490 N/mm²

E(1=5d): 22 – 28 %

I: 63 – 80 Joule

Table separator
Mo Kb
AWS: E 7018 A 1

DIN 8575: E Mo B 20+

-
Lime-basic coated electrode for high tensile and high temperature steel. The weld deposit is tough and non-ageing.
Table separator
Cromo 1 Ti
AWS: E 8013 G

ISO 3580: E 1 Cr Mo R

DIN 8575:E Cr Mo 1 R 22

BS: 2493 Type B

Current: = (+) / ~

C: 0,07 %

Si: 0,35 %

Mn: 0,65 %

Cr: 1 %

Mo: 0,5 %

Rutile basic coated electrode for high quality weld beads on boiler – resp. pipe steel and heat – treatable steel of similar alloy .

Suitable for following base materials:
13CrMo22, 15CrMo3, MoV42

At 720 ºC
T: 590 – 690 N/mm²

Y: 480 – 510 N/mm²

E(1=5d): 18 – 22 %
—————-
At 930 ºC
T: 480 – 590 N/mm²

Y: 340 – 390 N/mm²

E: 20 – 24 %

Table separator
Cromo 1 Kb
AWS: E 8018 B 2

ISO 3580:E 1 Cr Mo B

DIN 8575:E Cr Mo 1 B 20+

Lime basic coated electrode for high quality weld beads on boiler – resp. pipe steel and heat – treatable steel of similar alloy.
Table separator
Cromo 1 Ni Kb
AWS: E 11018 G

Basic coated electrode for high-tensile fine grain constructional steel . The weld deposit has high tensile strength and is resistant to cracks. Ductile up to -60 ºC.
Table separator
Cromo 2 Ti
AWS: E 9013 G

ISO 3580: E 2 Cr Mo R

DIN 8575:E Cr Mo 2 R 22

BS: 2493 Type C

Current: = (+) / ~

C: 0,07 %

Si: 0,35 %

Mn: 0,65 %

Cr: 2,3 %

Mo: 1 %

Rutile basic coated electrode for high temperature – stressed parts in boiler and pipeline construction at working temperatures up to 600 ºC.

Suitable for base materials:
10 Cr Mo 9 10, 10 Cr SiMoV 7

At 760 ºC
T: 630 – 680 N/mm²

Y: 490 – 540 N/mm²

E(1=5d): min 20 %

I: 80 Joule
————–
At 950 ºC
T: 540 – 640 N/mm²

Y: 440 – 490 N/mm²

E(1=5d): 20 %

I: 80 Joule

Table separator
Cromo 2 Kb
AWS: E 9018 B 3

ISO 3580: E 2 Cr Mo B

DIN 8575:E Cr Mo 2 B 20+

Lime basic coated electrode for high temperature – stressed parts in boiler and pipeline construction at working temperatures up to 600 ºC.
Table separator
Cromo 5 Kb
AWS: E 502 – 15

ISO 3580: E 5 Cr Mo B

DIN 8575: E Cr Mo 5 B 20+

Current: = (+) / ~

C: 0,07 %

Si: 0,5 %

Mn: 1 %

Cr: 5,1 %

Mo: 0,5 %

Lime basic coated electrode for high temperature -steel in boiler construction. The weld deposit is heat-treatable.

Suitable for following base materials:
10 CrMo 19 5
and the steel downpour identical to kind.

At 760 ºC
T: 640 – 730 N/mm²

Y: 490 – 540 N/mm²

E(1=5d): 18 – 22 %

I: 110 Joule
————-
At 960 ºC
T: 590 – 690 N/mm²

Y: 470 – 540 N/mm²

E(1=5d): 18 – 22 %

I: 110 Joule

Table separator

Latest News

Pages

Categories

  • No categories

Little About Us

Hello Read More »

Cheap Jerseys Cheap Jerseys/ Cheap Jerseys Cheap Jerseys Cheap Jerseys Cheap Jerseys Cheap Jerseys Cheap Jerseys Cheap Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys Wholesale Jerseys